Thermal Properties of Functionalised Metallocene Polypropylene Fibres

In this contribution blend metallocene polypropylene (mPP) fibres modified with 4, 8, 12 wt.% of copolyamide A and 4, 8, 12 wt.% of compatibiliser L were prepared. Copolyamide A consists of 85 wt.% of e-caprolactam and 15 wt.% of nylon salt of adipic acid and diethylenetriamine. Compatibiliser L is low molecular isotactic polypropylene grafted with maleineanhydride. Thermal properties of the components, blends and modified mPP fibres were evaluated. Fibres modified with both copolyamide A and compatibilizer were successfully spun and drawn, with the opposite being the case for mPP fibres modified only with copolyamide A without compatibiliser L, which were not spun, confirming the positive role of compatibiliser L. The modified fibres conserve their thermal characteristics - melting temperature, melting enthalpy and entropy in the whole interval of both additive concentrations evaluated. The positive influence of the compatibiliser was found from the point of melting enthalpy and melting entropy.

Przygotowano dla oceny włókna wykonane z mieszanek metalocenowanego polipropylenu modyfikowanego 4, 8 i 12% kopoliamidem A oraz 4, 8 i 12% kompatybilizatorem L. Kopoliamid A składa si. z 85% e-kaprolaktamu i 15% soli nylonowej kwasu adypinowego i dietylenotriaminy. Kompatybilizator L jest niskomolekularnym izotaktycznym polipropylenem szczepionym bezwodnikiem maleinowym. Oceniono właściwości termiczne składników i gotowych produktow. Z polimerow z zastosowaniem kompatybilizatora z łatwością wyprzędziono włókna, podczas gdy mieszanki polimerów bez udziału kompatybilizatora nie dały się prząść. Dla otrzymanych włókien analizowano temperaturę topnienia, entalpię i entropię dla całego zakresu stosowanych stężeń. Potwierdzono pozytywny wpływ zastosowanego kompatybilizatora.