Influence of Wave-Absorbing Functional Particles on the Electromagnetic Properties and Mechanical Properties of Coated Composites for Nickel Powders

In this subject, a single-layer coated composite for nickel powders was prepared using PU2540 polyurethane as the matrix, nickel powder as the wave-absorbing functional particle, and coating technology on plain cotton fabric. The influence of wave-absorbing functional particles on the dielectric, shielding effectiveness and mechanical properties of the single-layer coated composite for nickel powders was mainly analysed and compared. Results showed that the real and imaginary parts and loss tangent of the dielectric constant were all the largest when the iron powder was mixed with the nickel powder, and its polarizing ability, loss ability and attenuation ability with respect to electromagnetic waves were all the maximum. When the graphene was mixed with the nickel powder, the shielding attenuation ability with respect to electromagnetic waves was the best.

W ramach pracy przygotowano jednowarstwowy kompozyt powlekany żywicą poliuretanową zawierającą proszek niklu. Do przygotowania kompozytów użyto poliuretanu PU2540 jako matrycy i proszku niklu jako absorbującej fale cząstki funkcjonalnej oraz zastosowano technologię powlekania na gładkiej tkaninie bawełnianej. Przeanalizowano i porównano głównie wpływ absorbujących fale funkcjonalnych cząstek na dielektryk, skuteczność ekranowania i właściwości mechaniczne jednowarstwowego powlekanego kompozytu. Wyniki pokazały, że rzeczywiste i urojone części oraz styczna strat stałej dielektrycznej były największe, gdy proszek żelaza został zmieszany z proszkiem niklu, a jego zdolność polaryzacyjna, zdolność do strat i zdolność tłumienia fal elektromagnetycznych były maksymalne. Gdy grafen został zmieszany z proszkiem niklu, zdolność tłumienia ekranowania fal elektromagnetycznych była najlepsza.