Determination of Ressidual Pseudo-Chemical Energy and Energy Dissipative During Reversible Martensitic Transformation in Ni52,2Mn21,3Ga26,5 Alloy

In this paper we present results of an analysis of the influence of annealing time on the residual pseudo-chemical energy and dissipative energy Fdis(z) during reversible martensitic transformation. Analysis was performed without equilibrium temperature and basis on the model proposed in the study: (LIKHACHEV 1998). From designated courses of residual non-chemical and pseudo-chemical dissipative energies come, that carried thermal treatment causes significant changes of them. Immediately after casting the studied alloy shows continuous increase of the dissipative energy with increasing of martensite fraction. After annealing at the time from 1-0 h, curves Fdis(z) have a curse close to constant function whereas beyond this range show dynamic increasing or decreasing of dissipation energy.

W pracy przedstawiono wyniki przeprowadzonej analizy wpływu czasu wygrzewania próbek stopu Ni52,2Mn21,3Ga26,5 na resztkową energię sprężystą oraz energię dyssypowaną Fdis(z) podczas odwracalnej przemiany martenzytycznej. Analizę przeprowadzono z pominięciem temperatury równowagi fazowej na podstawie modelu zaproponowanego w pracy LIKHACHEVA (1998). Z wyznaczonych przebiegów zmian resztkowej energii sprężystej oraz energii rozpraszanej wynika, że przeprowadzona obróbka termiczna powoduje znaczne ich zmiany. W stanie bezpośrednio po wytopie badany stop wykazuje ciągły wzrost energii rozpraszanej wraz ze wzrostem zawartości frakcji martenzytu. Po zastosowaniu wygrzewania w czasach 1-20 h, krzywe Fdis(z) mają przebieg zbliżony do funkcji stałej, natomiast poza nim wykazują dynamiczny wzrost bądź spadek energii dyssypowanej.