The B-Li System. Calorimetric and Theoretical Studies

The standard enthalpy of formation of the B₇₈Li₂₂ alloy was measured with the use of the water reaction calorimetric method at 25 °C (298 K). An X-ray diffraction study of the prepared sample was conducted. The obtained diffraction pattern was different from the patterns for the B3Li and B₁₄Li₃ phases. The standard enthalpy of formation obtained for the B₇₈Li₂₂ alloy was -39.0 ± 0.7 kJ/mole of atoms. This value corresponds well with the formation enthalpies of the phases from the boron-lithium system. Theoretical calculations of the standard enthalpy of formation were conducted for the B₇₈Li₂₂ alloy and the phases from B-Li system, which were investigated earlier. A discussion of the deviations observed between both sets of data (experimental and calculated) was performed. Additionally, DTA studies were performed for 14 alloys of the concentrations from 40 to 100 at. % of Li.

Standardowa entalpia tworzenia stopu B78Li22 została zmierzona metodą kalorymetrii reakcyjnej wodnej. Próbka stopu po wyżarzaniu była poddana badaniom strukturalnym metodą dyfrakcji promieniowania rentgenowskiego. Uzyskany dyfraktogram jest inny od dyfraktogramów dla faz B3Li ora B14Li3. Zmierzona standardowa entalpia tworzenia stopu B78Li22 wyniosła -39.0 ± 0.7 kJ/mol atomów. Wartość ta dobrze koreluje z entalpią tworzenia faz z układu bor-lit. Przeprowadzone zostały również obliczenia teoretyczne standardowej entalpii tworzenia dla stopu B78Li22 oraz faz z układu B-Li, wcześniej badanych. Zaobserwowane rozbieżności między teoretycznymi i eksperymentalnymi wartościami entalpii tworzenia zostały przedyskutowane. Ponadto, wykonano pomiary DTA dla 14 stopów o stężeniach od 40 do 100 % at. Li.