Injection molding of transparent polymeric materials with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide forenhanced fire retardancy

Selected transparent polymers [i.e., polystyrene (PS) and poly(methyl methacrylate) (PMMA)] were extruded with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO). The obtained compositions were formed into testing samples by injection molding process. The obtained materials (containing 1–10 wt parts/100 wt parts of the polymer) exhibited higher melt flow rate and thermal resistance, as well as reduced flammability (while maintaining their mechanical properties). Additionally, Fourier transform infrared spectroscopy (FT-IR) analysis of modified polymers was conducted. Studies confirmed that – during the extrusion and/or injection molding – DOPO reacts with PS and PMMA.

Wybrane transparentne polimery termoplastyczne [tj. polistyren (PS) i poli(metakrylan metylu) (PMMA)] wytłaczano z 10-tlenkiem 9,10-dihydro-9-oksa-10-fosfafenantrenu (DOPO), a z uzyskanych kompozycji metodą wtrysku formowano próbki do badań. Otrzymane materiały (zawierające 1–10 cz. mas. DOPO/100 cz. mas. polimeru) charakteryzowały się większym wskaźnikiem szybkości płynięcia, większą odpornością termiczną oraz mniejszą zapalnością (przy zachowaniu właściwości mechanicznych) niż polimery niemodyfikowane. Dodatkowo kompozycje z DOPO oceniano metodą spektroskopii w podczerwieni z transformacją Fouriera (FT-IR). Badania potwierdziły, iż w trakcie wytłaczaniai/lub formowania wtryskowego DOPO reaguje z PS oraz PMMA.