Synthesis and characterization of high-molar-mass star-shaped poly(l-lactide)s

The synthesis of high-molar-mass linear and 6-arm star-shaped poly(l-lactide)s(PLLA’s) is presented. Dipentaerythritol and benzyl alcohol were used asinitiators and Sn(Oct)2 was applied asa catalyst in the ring-opening polymerization (ROP) of l-lactide (l-LA) carried out at 130 °C. The prepared PLLA’s were characterized by SEC (size exclusion chromatography), 1H NMR (proton nuclear magnetic resonance spectroscopy), DSC (differential scanning calorimetry), and TGA (thermogravimetric analysis). The structure of the obtained star-shaped polymers was confirmed by comparison of the radii of gyration (Rg) determined by SEC for the linear and star macromolecules. The thermal properties of PLLA’s were shown for the wide range of molar masses. Additionally, it was confirmed that Irganox stabilizer has an influence on the thermal stability of PLLA’s.

Przedstawiono syntezę liniowych i 6-ramiennych gwiaździstych poli(l-laktydów)(PLLA) o dużych masach molowych. Polimeryzację z otwarciem pierścienia (ROP) l-laktydu(l-LA) inicjowaną dipentaerytrytem oraz alkoholem benzylowym prowadzono w temperaturze130 °C wobec Sn(Oct)2 jako katalizatora. Otrzymane PLLA scharakteryzowano za pomocą SEC (chromatografia żelowa), 1HNMR (spektroskopia magnetycznego rezonansu jądrowego), DSC (różnicowa kalorymetria skaningowa) i TGA (analiza termograwimetryczna). Strukturę otrzymanych polimerów gwiaździstych potwierdzono przez porównanie wyznaczonych w SEC promieni bezwładności (Rg) dla gwiaździstych iliniowych makrocząsteczek. Właściwości termiczne PLLA przedstawiono dla szerokiego zakresu mas molowych. Dodatkowo potwierdzono, że stabilizator Irganox ma wpływ na stabilność termiczną PLLA.