The effect of niobium and titanium in base metal and filler metal on intergranular corrosion of stainless steels

The article describes the effect of alloyed additives in base material and filler metal on intergranular corrosion. Steel 1.2 mm thick, titanium-stabilized ferritic stainless steel and titanium and niobium-stabilized ferritic stainless steel have been surfacing method MAG (135). The specimens received was subjected to macro and microscopic tests, hardness tests and the intergranular corrosion resistance test. The study showed a higher corrosion resistance of niobium and titanium stabilized steel from titanium-stabilized steel. In addition, a ferritic fine-grain structure was found in the padding axis made with the use of filler metal with titanium and niobium microadditives.

W artykule opisano wpływ dodatków stopowych w materiale rodzimym i spoiwie na korozje międzykrystaliczną. Blachy o grubości 1,2 mm ze stali nierdzewnej ferrytycznej stabilizowanej tytanem oraz stali nierdzewnej ferrytycznej stabilizowanej tytanem i niobem zostały napawane metodą MAG (135). Otrzymane próbki poddano badaniom makro i mikroskopowym, zmierzono twardość oraz przeprowadzono badania odporności na korozje międzykrystaliczną. W wyniku przeprowadzonych badań stwierdzono wyższą odporność korozyjną stali stabilizowanej niobem i tytanem od stali stabilizowanej tylko tytanem. Ponadto, wykazano występowanie struktury drobnoziarnistej ferrytycznej w osi napoiny wykonanej przy użyciu materiału dodatkowego z mikrododatkami tytanu i niobu.