Wood plastic composites as a substitution for HDF

Wood plastic composites as a substitution for HDF. As part of the research, industrial HDF boards were used and WPC composites were produced, differentiated in terms of matrix (PLA and HDPE) and filler content (40%, 50% and 60%). The density and density profile was measured to compare HDF and WPC structure. In addition, the manufactured boards were tested for strength (MOR, MOE), screw holding, thickness swelling and water absorption after immersion in water for 2 and 24 hours. WPC were characterized by a higher density than HDF boards and a uniform density profile. In addition, WPC composites were characterized by lower MOR and MOE values than HDF boards. Compared to HDF boards, WPC composites were characterized by higher values of screw holding and better resistance to moisture.

Kompozyty WPC jako substytut płyt HDF. W ramach badań wykorzystano przemysłowe płyty HDF oraz wytworzono kompozyty WPC zróżnicowane pod kątem matrycy (PLA i HDPE) oraz udziału napełniacza (40%, 50% i 60%). Oznaczono gęstość i profil gęstości w celu porównania struktury HDF i WPC. Ponadto wytworzone płyty zostały przetestowane pod kątem wytrzymałości (MOR, MOE), utrzymania wkrętów, spęcznienia na grubość oraz nasiąkliwości po moczeniu w wodzie przez 2 i 24 godziny. WPC charakteryzowały się wyższa gęstością niż płyty HDF oraz jednorodnym profilem gęstości. Ponadto kompozyty WPC charakteryzowały się niższymi wartościami MOR i MOE niż płyty HDF. W porównaniu do płyt HDF kompozyty WPC charakteryzowały się wyższymi wartościami zdolności utrzymania wkrętów oraz lepszą odpornością na działanie wilgoci.