The effect of nitrogen ion implantation on nano-scale hardness and elastic modulus of WC-Co indexable knives for wood materials machining

The effect of nitrogen ion implantation on nano-scale hardness and elastic modulus of WC-Co indexable knives for wood materials machining. The paper presents the results of a study investigating the effects of nitrogen ion implantation into the surface layer of WC-Co blades, used for machining wood materials, on their hardness and modulus of elasticity at the nano-scale. The modified blades were analyzed in six variants of implantation process parameters, and compared with control blades (virgin, unmodified). Three energies of accelerating nitrogen ions were used in the implantation process (5, 50 and 500 keV) and two doses of implanted ions (1e17 and 5e17 cm-2). The nano-hardness and elastic modulus of all blades were measured using an Anton Paar TriTec (UNHT) hardness tester.

Wpływ implantacji jonów azotu na twardość i moduł sprężystości w nano-skali noży wymiennych WC-Co do obróbki materiałów drzewnych. W artykule przedstawiono wyniki wpływu procesu implantacji jonów azotu do warstwy wierzchniej ostrzy WC-Co do obróbki materiałów drzewnych na ich twardość i moduł sprężystości w nano-skali. Analizowano ostrza modyfikowane w sześciu wariantach parametrów procesu implantacji, oraz w celach porównawczych, ostrza kontrolne (niemodyfikowane). Zastosowano trzy energie przyspieszenia jonów azotu w procesie implantacji (5, 50 i 500 keV) oraz dwie dawki implantowanych jonów (1e17 oraz 5e17 cm-2). Pomiaru twardości i modułu sprężystości w nano-skali wszystkich ostrzy dokonano przy użyciu twardościomierza Anton Paar TriTec (UNHT).