Influence of elevated temperature on low cycle properties of WCLV/1.2344 steel

In this paper the results of low cycle fatigue tests of hot-work tool WCLV (1.2344) steel carried out at the temperatures of 20ºC and 600°C were presented. These results are used for numerical modelling of the wearing course of forging tools. This analysis was performed by means of hysteresis loop parameters recorded during tests. It was stated that the elevated temperature influences fatigue life and changes of hysteresis loop parameters in the function of loading cycles. At the temperature of 600°C, changes in the parameters were significantly higher than at 20°C. It make mare difficult to calculate the fatigue life of objects operating at elevated temperatures, because materiał data determined during tests reflects only the momentary properties of steel.

W pracy zamieszczono wyniki niskocyklowych badań zmęczeniowych stali WCL V 1.2344 w temperaturze 20°C oraz 600°C. Analizę wyników prowadzono przy wykorzystaniu parametrów pętli histerezy rejestrowanych w trakcie badań. W pracy stwierdzono, że podwyższona temperatura ma wpływ na trwałość zmęczeniową oraz zmiany parametrów pętli w funkcji liczby cykli obciążenia. W temperaturze 600°C zmiany parametrów są zdecydowanie większe niż w temperaturze 20°C. Utrudnia to prowadzenie obliczeń trwałości obiektów poddanych eksploatacji w temperaturze podwyższonej. Wyznaczone podczas badań dane materiałowe odzwierciedlają bowiem jedynie chwilowe właściwości stali.