Characteristics of Al-Fe sinters made by the powder metallurgy route

The Al/Fe material was prepared by the powder metallurgy route with an additional intermediate stage which was a centrifuge of powder mixture. The application of the centrifuge stage was applied to obtain circular phase distribution of Al-rich phases in a sintered material. Iron powder with a particle size under 100 μm and aluminum powder with a particle size of about 25 μm, were used as starting materials. To determine the effect of centrifuging time on the distribution of Fe-Al particles, scanning electron microscopy (SEM, EDS) and XRD techniques were used. Microstructure observations show the influence of the centrifuging time on the distribution of Fe particles. It was observed that a longer centrifuging time caused changes in the ratio concentration of elements and allowed the growth of the intermetallic phase at the interface between solid Al and Fe particles.

Spiekane materiały Al/Fe wytwarzano metodą metalurgii proszków z wprowadzeniem etapu pośredniego w postaci odwirowania mieszaniny proszku. Etap wirowania miał na celu uzyskanie kulistego rozkładu faz bogatych w Al w spiekanym materiale. Proszek żelaza o wielkości cząstek poniżej 100 μm i proszek aluminium o wielkości cząstek około 25 μm zastosowano jako materiały wyjściowe. W celu określenia wpływu czasu wirowania mieszanki na rozkład faz w wytworzonym materiale zastosowano techniki skaningowej mikroskopii elektronowej (SEM, EDS) i dyfraktometrii rentgenowskiej (XRD). Obserwacje mikrostruktury wykazały istotny wpływ czasu wirowania na mikrostrukturę uzyskanych spieków. Zaobserwowano, że dłuższy czas wirowania spowodował zmianę stosunku stężenia pierwiastków i pozwolił na wzrost fazy międzymetalicznej na granicy faz między stałymi cząstkami Al i Fe. Badania mikrotwardości obszarów spiekanego materiału świadczą o zwiększeniu twardości w obszarach nowo utworzonych faz międzymetalicznych.