Influence of addition of a mixture of manganese and iron carboxylate on the degradation process of LDPE films

A study was made of the degradation of polyethylene packaging film modified with Mn(II) and Fe(III) carboxylate at additive content of 0.5 and 1 wt%. A comparison was made between the effectiveness of manganese and iron carboxylate at molar ratio of Mn: Fe 1.5 and the photodegradative effects of mixed carboxylate salts of these metals of various content of the individual fatty acids. We compared the effects of degradation of films obtained under the same processing variables and aged under the same conditions. In this way we have studied the effect of chemical composition of the carboxylates on their effectiveness and the usefulness of technical grade stearin in obtaining an effective and thermally durable prodegradant.

Przedstawiono wyniki badań degradacji opakowaniowej folii polietylenowej modyfikowanej karboksylanami Mn(II) i Fe(III) przy zawartości tego dodatku w polimerze 0.5 i 1% mas. Porównano skuteczność karboksylanu manganu i żelaza o stosunku molowym Mn:Fe 1.5 na działanie fotodegradacyjne mieszanych soli karboksylowych tych metali o różnym składzie indywidualnych kwasów tłuszczowych. Porównano efekty degradacji folii uzyskanych w tych samych warunkach przetwórstwa i poddawanych starzeniu. Badano wpływ składu chemicznego karboksylanów na ich skuteczność oraz przydatność stearyny technicznej do uzyskania skutecznego i termicznie trwałego prodegradanta.