Possibilities of Reclamation Microwave-Hardened Molding Sands with Water Glass

The paper presents results of a research on identifying opportunities for effective reclamation of waste molding sand with water-glass, hardened by microwave heating. The molding sand applied in the tests was prepared with use of selected type 145 of sodium water-glass. The sand was sequentially processed by microwave hardening, cooling, thermal loading to 800°C, cooling to ambient temperature, crushing and mechanical reclamation. These stages create a closed processing loop. After each cycle, changes of tensile strength and bending strength were determined. Results of the study show that it is possible to activate surface of high-silica grains of waste foundry sand hardened with microwaves, provided that applied are appropriate processing parameters in successive operation cycles.

W pracy przedstawiono wyniki badań nad określeniem możliwości prowadzenia skutecznej regeneracji zużytych mas formierskich ze szkłem wodnym utwardzanych w procesie nagrzewania mikrofalowego. Przeznaczoną do badań masę, sporządzoną z wybranym szkłem wodnym sodowym gatunku 145, poddawano kolejno procesom: utwardzania mikrofalowego, studzenia, obciążaniu termicznemu do temperatury 800°C. studzenia do temperatury otoczenia, rozkruszania i regeneracji mechanicznej. Opisane procesy tworzyły jeden zamknięty cykl przerobu zużytej masy. Po każdym kolejnym cyklu przerobu masy określano zmianę wytrzymałości na rozciąganie i zginanie. Analizując wyniki przeprowadzonych badań stwierdzono, że istnieje możliwość aktywacji regeneratu zużytej masy formierskiej ze szkłem wodnym, utwardzanej w procesie nagrzewania mikrofalowego, pod warunkiem zastosowania odpowiednich parametrów jej przygotowania, odbywającego się w kolejnych cyklach eksploatacji.