The effect of sintering temperature on microstructure and properties of Al - SiC composites

Attempts have been made to describe the influence of sintering temperature on the microstructure and properties of Al - SiC composites. Mixtures of 100%Al and Al - 5% SiC, Al - 10% SiC were produced by tumbling for 30 minutes in the Turbula T2F mixer. The powders were subsequently cold pressed at pressure 300MPa in a rigid die on a single action press. The green compacts were sintered in nitrogen at 580°C and 620°C for one hour. The main objective of this work was to determine influence of chemical composition and the manufacturing parameters on microstructure and properties of Al - SiC composites produced by powder metallurgy technology.

W pracy przedstawiono wyniki badań kompozytów aluminiowych umacnianych cząstkami węglika krzemu SiC. Wytworzono spiekane kompozyty o zawartości 5% i 10% SiC. Jako materiał referencyjny stosowano Al99,7 wytworzone w takich samych warunkach, jak kompozyty Al - SiC. Materiały wytworzono na drodze jednostronnego prasowania przy zastosowaniu ciśnienia prasowania 300MPa. Kolejno kształtki poddano spiekaniu w atmosferze azotu w temperaturze 580 C oraz 620 C. Na tak wytworzonych spiekach przeprowadzono obserwacje mikrostruktury, pomiar twardości metoda Brinella, próbę zginania oraz przy zastosowaniu testera T05 badanie odporności na zużycie ścierne. Celem pracy jest określenie wpływu składu chemicznego oraz parametrów procesu wytwarzania na mikrostrukturę i właściwości kompozytów Al - SiC wytwarzanych technologia metalurgii proszków.