Codeposition of SiC particles with electrolytic nickel

Ni/SiC composite coatings were produced by electrodeposition from chloride-sulphate bath. The effect of SiC concentration on the percentage of embedded particles at two current densities (0.75 and 1.50 Aźdm-2) was determined. SiC content in the nickel matrix was in the range of 13-23 vol%, but lower values were found for higher current density. Increased particles contents in the coatings practically did not change microhardness of deposits (approximately 300 HV), but it increased corrosion resistance. Morphology and particle distribution in the deposits was studied with optical and transmission electron microscopes. Specific surface charge of SiC particles as well as adsorption of Ni2+ions on the powder particles were also determined.

Powłoki kompozytowe Ni/SiC otrzymywano na drodze elektrolizy z zastosowaniem kąpieli chlorkowo-siarczanowej. Określono wpływ stężenia SiC na skład osadów katodowych uzyskiwanych przy dwóch gęstościach prądu (0.75 and 1.50 Aźdm-2). Udział SiC w osnowie niklowej wynosił 13-23 %obj., przy czym niższe zawartości stwierdzono w powłokach otrzymanych przy wyższej gęstości prądu. Wzrost zawartości fazy dyspersyjnej w osadach katodowych nie wpływa na mikrotwardość kompozytów (ok. 300 HV), następuje natomiast wzrost ich odporności korozyjnej. Morfologię powierzchni i rozkład cząstek dyspersyjnych w osnowie niklowej określano na podstawie obserwacji mikroskopowych. Wyznaczono ładunek powierzchniowy cząstek SiC oraz wielkość adsorpcji jonów Ni2+.