Dielectric and mechanical properties of BaBi2(Nb0.99V0.01)2O9 Ceramics

The BBN ceramics doped by vanadium have been broadly recognized by using nano indentation techniques and ultrasound velocity and measurements. The results affirm that the vanadium admixture significantly improved the mechanical quality of ceramics. Such a small dopant doesn't change the dielectric properties, but we obtain visible increasing of the dielectric permittivity value and shifts the temperature of the ?max to higer values. The vanadium admixture decreased the diffusion degree ? as well as influenced on the parameters characteristic for the relaxor behaviour. Our suggestion is that partial substitution of the smaller vanadium ions into the niobium sites renders for example ordering of the dipoles.

Własności mechaniczne ceramiki BBN domieszkowanej wanadem były szeroko badane przy użyciu zarówno techniki nanoindentacji, jak i pomiaru prędkości rozchodzenia się fal ultradźwiękowych w materiale. Otrzymane wyniki potwierdziły przypuszczenie, że domieszka wanadu znacznie poprawia własności mechaniczne ceramiki. Tak mała ilość domieszki nie wpływa w znaczący sposób na własności dielektryczne ceramiki, jednak wpływ ten jest zauważalny. Mianowicie wzrasta wartość maksymalna przenikalności dielektrycznej przy jednoczesnym przesunięciu odpowiadającej jej temperatury ku wyższym wartością. Ponadto domieszka wanadu powoduje zmniejszenie stopnia rozmycia przejścia fazowego oraz wpływa na własności relaksorowe ceramiki.