Recovery of Tellurium From Sodium Carbonate Slag

This study is devoted to tellurium recovery from sodium carbonate slag, formed in the fire refining process of crude silver. The slag was modified by silica additions and then reduced by carbon oxide. The degree of the slag modification was defined by the parameter kw. The compositions of the investigated slag determined by the parameter kw and the mole fraction of the tellurium oxide (x_TeO2) are given in the following Table. The reduction of tellurium was very fast for all the investigated slags, which was manifested by an almost complete conversion of CO into CO₂. Unfortunately, at the same time, a side reaction took place, and as a results sodium telluride was formed, which reported to the slag: (Na₂O)_slag+ Te_g + CO = (Na₂Te)_slag + CO₂. The tellurium content in the reduced slag decreases as the parameter kw increases, and only the slag with the kw equal unity was suitable for the tellurium recovery in form of dusts, containing more than 76 wt-% tellurium.

Praca jest poświęcona odzyskowi telluru z żużla sodowego, który tworzy się podczas rafinacji ogniowej srebra. żużel ten był modyfikowany dodatkiem krzemionki, a następnie poddawany redukcji za pomocą tlenku węgla. Stopień modyfikacji żużla określał parametr kw. Składy badanych żużli wyrażonych za pomocą parametru kw oraz ułamka molowego tlenku telluru (x_TeO2) zawiera poniższa tabela. Redukcja telluru przebiegała bardzo szybko w przypadku każdego z badanych żużli, co przejawiało się poprzez prawie kompletna konwersje CO do CO₂. Niestety, w tym samym czasie przebiegała reakcja uboczna w wyniku której tworzył się tellurek sodu, który rozpuszczał się w żużlu: (Na₂O)_uel+ Te_g + CO = (Na₂Te)_uel + CO₂Stężenie telluru w żużlu malało wraz ze wzrostem parametru kw. Ale dopiero żużel charakteryzujący się parametrem kw = 1 okazał się odpowiedni do odzysku telluru, który przechodził do pyłów zawierających ponad 76% telluru.