The equal channel angular extrusion process of multiphase high strength aluminium bronze

The aim of the research was to determine the deformation condition of ECAP process of multiphase high strength aluminium bronze BA1032. The studies have indicated that it is possible to deform multiphase aluminium bronze BA1032 in the ECAP process at a temperature of 400°C and die angle Φ=110°. The deformation of the bronzes at lower temperatures encounters some difficulties - cracks appear which make repeated ECAP impossible. The cracks appear on the top surface of the samples where it contacts the surface of the outlet channel. FEM simulations show that the largest plastic strains occur in this area. The proposed ECAP method of large plastic deformations as applied to the investigated aluminium bronzes makes it possible to obtain very strong refinement especially of eutectoid α+ γ2.

Celem pracy było określenie warunków odkształcania w procesie ECAP wysokowytrzymałych wielofazowych brązów aluminiowych. Przeprowadzone badania wskazują na możliwość odkształcania wielofazowych brazów aluminiowych w tym procesie w temperaturze 400 °C dla kąta matrycy Φ=110°. Pewne trudności sprawia odkształcanie brązu w niższych temperaturach, gdyż pojawiają się wówczas pęknięcia, które uniemożliwiają prowadzenie procesu wielokrotnego przeciskania próbek przez kanał katowy. Pęknięcia pojawiaja sie na górnej powierzchni próbek w miejscu kontaktu z powierzchnią kanału wyjsciowego. Jak wykazuje symulacje MES w miejscu tym występują największe odkształcenia plastyczne. Zastosowana metoda dużych odkształceń plastycznych ECAP w przypadku badanych brazów aluminiowych pozwala uzyskać bardzo silne rozdrobnienie głównie eutektoidu α+ γ 2.