Mechanical Spectroscopy of MgB2 Containing SiC

The compound magnesium diboride (MgB₂) has been well-known since the 1950s; however, its superconducting properties were unknown. Intrinsic characteristics of MgB₂ make this material a promising candidate for technological applications, although the low value of the irreversibility field and the decrease in critical current density with the increase in the magnetic field considerably reduce its utility. The present work aimed to study the effect of carbon-based doping on anelastic properties of MgB₂ as measured by mechanical spectroscopy. The samples were prepared by using the powder-intube method. The samples were made with 5, 7.5, and 10 wt.% of silicon carbide (SiC). The results reveal complex mechanical loss spectra caused by the interaction between point defects and surface defects in the crystalline lattice of MgB₂.

Dwuborek związek magnezu (MgBV) jest znany od 1950 roku; jednak jego właściwości nadprzewodzące były nieznane. Swoiste cechy MgB₂ czynią ten materiał obiecującym kandydatem do zastosowań technicznych, jednak niskie wartości nieodwracalnego pola i zmniejszenie krytycznej gęstości prądu ze wzrostem pola magnetycznego znacznie zmniejszają jego użyteczność. Celem pracy było zbadanie wpływu domieszkowania związkiem węgla na anelastyczne właściwości MgB₂ mierzone metodą spektroskopii mechanicznej. Próbki zostały przygotowane za pomocą metody powder-in-tube (PIT). Wytworzono próbki o zawartości 5, 7.5 i 10 % wag. węglika krzemu (SiC). Wyniki pokazują złożone widma strat mechanicznych powodowanych przez wzajemne oddziaływanie pomiędzy defektami punktowymi i defektami powierzchniowymi w sieci krystalicznej MgB₂.