Prediction of the Mechanical Properties of Chrome-Nickel Austenitic Stainless Steels with Respect to their Chemical Composition

The research was concerned with the influence of chemical composition of austenitic steels on their mechanical properties. Resulting properties of castings from austenitic steels are significantly influenced by the solidification time that affects the size of the primary grain as well as the layout of elements within the dendrite and its parts with regard to the last solidification points in the interdendritic melt. During solidification an intensive segregation of all admixtures occurs in the melt, which causes a whole range of serious metallurgical defects and it has also a significant influence on subsequent precipitation of carbides and intermetallic phases. Chemical heterogeneity then affects the structure and mechanical properties of the casting. In a planned experiment, we cast melted steels containing 18 to 28 % Cr and 8 to 28 % Ni with variable carbon and nitrogen contents. Testing the tensile strength of the cast specimens we could determine the Rp0.2, Rm, and A5 values. The dependence of the mechanical properties on the chemical content was described by regression equations. The planned experiment results allow us to control the chemical content for the given austenitic steel quality to achieve the required values of the mechanical properties.