The rheological properties of coal bitumens modified by polyesters.

The purpose of testing was to find changes of rheological properties of coal-tar pitch (CTP) due to modification with chosen polyesters. Poly(ethylene terephthalate) (PET), unsaturated polyester resin (UP) and polycarbonate (PC) were selected for testing. Polymers, in the amounts of 10 and 25 wt %, were mixed with CTP under conditions considered optimal for each modifier type. Properties of CTP-polymer compositions were assessed based on their softening point, content of components insoluble in toluene and quinoline and on rheological properties. Distinct changes of rheological properties, especially changes in viscosity versus shear rate and temperature, as well as viscoelastic properties were observed as results of modifications with all used polyesters. The modification effects became more intensive with increasing amount of the modifier added to CTP.

Celem badań było określenie zmian właściwości reologicznych paku węglowego (CTP) na skutek modyfikacji poliestrami: poli(tereftalanem etylenu) (PET), nienasyconą żywicą poliestrową (UP) oraz poliwęglanem (PC). Polimery te, w ilości 10 i 25 % mas. mieszano z pakiem w warunkach uznanych za optymalne dla każdego rodzaju modyfikatora. Właściwości kompozycji CTP-polimer oceniono na podstawie ich temperatury mięknienia, zawartości składników nierozpuszczalnych w toluenie i chinolinie oraz właściwości reologicznych. W przypadku każdego poliestru modyfikacja powodowała wyraźne zmiany właściwości reologicznych, w tym zmiany lepkości ze wzrostem szybkości ścinania i temperatury oraz właściwości lepkosprężystych. Efekty modyfikacji nasilały się ze zwiększeniem ilości modyfikatora dodawanego do CTP.